Cut
Core Design Manual
MATERIAL CODES AND TEST POINTS: TABLE 3
|
TABLE III -
MATERIAL CODES AND TEST POINTS
|
|
MATERIAL
|
GAGE
|
STACKING
FACTOR
|
MATERIAL
CODE
|
B MAX KILOGAUSS
|
TEST
POINT
|
TYPICAL
DATA
|
|
B(KG)
|
f (HZ)
|
W/LB
|
VA/LB
|
|
MICROSIL
|
1 mil
|
.83
|
MM
|
15.0
|
10
|
400
|
8.0
|
16.5
|
|
2 mil
|
.89
|
ML
|
16.0
|
15
|
400
|
12.7
|
20.0
|
|
4 mil
|
.90
|
MH
|
17.0
|
15
|
400
|
10.0
|
13.1
|
|
4 mil
|
.90
|
MTH*
|
17.0
|
15
|
400
|
12.0
|
22.0
|
|
4 mil
|
.90
|
MZ
|
18.0
|
17.6
|
400
|
16.9
|
48.0
|
|
4 mil
|
.90
|
MTZ*
|
18.0
|
17.6
|
400
|
18.0
|
68.0
|
|
7 mil
|
.90
|
MJ
|
18.0
|
17.6
|
400
|
15.0
|
30.0
|
|
7 mil
|
.90
|
MTJ*
|
18.0
|
17.6
|
400
|
17.0
|
50.0
|
|
9 mil
|
.95
|
MAZ, MSZ
|
18.0
|
17.6
|
60
|
1.1
|
2.1
|
|
9 mil
|
.95
|
MTAZ, MTSZ*
|
18.0
|
17.6
|
60
|
1.2
|
2.6
|
|
12 mil
|
.95
|
MA
(<10 LB.)
|
18.0
|
15.0
|
60
|
.9
|
1.7
|
|
12 mil
|
.95
|
MS(>10
LB.)
|
18.0
|
15.0
|
60
|
.9
|
1.7
|
|
12 mil
|
.95
|
MTA, MTS*
|
18.0
|
15.0
|
60
|
1.1
|
2.5
|
|
Supermendur
|
4 mil
|
.90
|
MXH
|
21.0
|
21.0
|
400
|
15.0
|
36.0
|
|
4 mil
|
.90
|
MTXH*
|
21.0
|
21.0
|
400
|
20.0
|
62.0
|
|
Superperm 49
|
1 mil
|
.83
|
MBM
|
15.0
|
12.0
|
400
|
3.0
|
3.5
|
|
2 mil
|
.89
|
MBL
|
15.0
|
12.0
|
400
|
3.8
|
4.0
|
|
4 mil
|
.90
|
MBH
|
15.0
|
12.0
|
400
|
4.2
|
4.5
|
|
6 mil
|
.90
|
MBG
|
15.0
|
12.0
|
400
|
4.5
|
4.8
|
|
Superperm 80
|
1 mil
|
.83
|
MCM
|
7.0
|
4.0
|
400
|
0.18
|
0.70
|
|
2 mil
|
.89
|
MCL
|
7.0
|
4.0
|
400
|
0.20
|
0.70
|
|
4 mil
|
.90
|
MCH
|
7.0
|
4.0
|
400
|
0.25
|
0.75
|
|
6 mil
|
.90
|
MCG
|
7.0
|
4.0
|
400
|
0.30
|
0.80
|
* For Three Phase MT - Cores: Testing will be performed under single conditions
and totaled to replicate three phase conditions. The exception to this test method
would be when a customer provides a set of three phase.
|
|